Alloy20,NS1403,2.4660 奧氏體鐵鎳基耐蝕合金
Alloy20,NS1403,2.4660 奧氏體鐵鎳基耐蝕合金
20合金(Alloy20)是一種奧氏體型鎳鐵鉻基超級(jí)合金,可同時(shí)視為不銹鋼和鎳基合金。
詳情請(qǐng)登入http://m.2008jx.com
標(biāo)準(zhǔn)對(duì)照
中國 |
GB/T 15007 GB/T 15008 YB/T 5353 YB/T 5354 |
NS1403(NS143) 0Cr20Ni35Mo3Cu4Nb |
美國 |
Special Metals |
INCOLOY® alloy 020 |
CARPENTER |
CarTech® 20Cb-3® |
|
ASTM B473 ASTM B462 ASTM B463 ASTM B464 ASTM B468 |
UNS N08020 |
|
ASTM A182 |
F20(鍛造) |
|
德國 |
VDM Metals |
Nicrofer ® 3620 Nb |
DIN 17744 DIN 17750 DIN 17751 DIN 17752 DIN 17753 |
NiCr20CuMo 2.4660 |
成分規(guī)范
牌號(hào) |
NS1403 |
N08020 |
2.4660 |
C |
≤0.07 |
≤0.07 |
≤0.07 |
Si |
≤1.00 |
≤1.00 |
≤1.00 |
Mn |
≤2.00 |
≤2.00 |
≤2.00 |
P |
≤0.030 |
≤0.045 |
≤0.025 |
S |
≤0.030 |
≤0.035 |
≤0.015 |
Ni |
32.0~38.0 |
32.0~38.0 |
32.0~38.0 |
Cr |
19.0~21.0 |
19.0~21.0 |
19.0~21.0 |
Mo |
2.0~3.0 |
2.0~3.0 |
2.0~3.0 |
Cu |
3.0~4.0 |
3.0~4.0 |
3.0~4.0 |
Nb |
8×C~1.0 |
Nb+Ta: 8×C~1.0 |
Nb+Ta: 8×C~1.0 |
Co |
— |
— |
≤1.5 |
Fe |
余量 |
Remainder |
Other |
材料性能
① 含有氯化物、硫酸、磷酸和硝酸的化學(xué)品中,具有優(yōu)異的抗全面腐蝕、晶間腐蝕、點(diǎn)蝕和縫隙腐蝕的能力。耐腐蝕性能介于316L不銹鋼和哈氏合金之間。在某些胺設(shè)施中耐蝕性不如316L不銹鋼,因?yàn)槿菀咨涉囦@絡(luò)化物。
②極低的碳含量,加上鈮元素有助于減少熱影響區(qū)碳化物的析出,因此在大多數(shù)情況下可以在焊接狀態(tài)下使用。除了氧乙炔外,所有常用的焊接方法都可以成功應(yīng)用。
③良好的冷成型性,可進(jìn)行半徑為兩倍于材料厚度的彎曲,以及拉伸壓制等成型操作。
④在高達(dá)500℃的環(huán)境中也具有優(yōu)異的機(jī)械性能。
應(yīng)用場合
20合金最初是在1951年為在硫酸中應(yīng)用而開發(fā)的,是硫酸工業(yè)環(huán)境****合金。在20%~40%的沸騰硫酸中,其表現(xiàn)出優(yōu)異的抗應(yīng)力腐蝕開裂性能。因?yàn)榉欠驳哪透g性能,20合金現(xiàn)在也是化工、食品、制藥和塑料等眾多行業(yè)的熱門選擇,并且作為高溫合金用于換熱器、混合罐、金屬清洗和酸洗設(shè)備以及管道。